High-Resistance Composite Laminated Shims
X.FIBER® Laminated Shims: Technical Information |
||||
|---|---|---|---|---|
Letter - Inch
113 KB
A4 - Metric
113 KB
Characteristics of X.Fiber® laminated shims |
| Properties | Values | Units | Test Conditions |
|---|---|---|---|
| Resistance to Traction | 460 | Mpa | ASTM D 3039-76 |
| Extension to Rupture | 3 | % | ASTM D 3039-76 |
| Traction Modulus | 15 | Gpa | ASTM D 3039-76 |
| Resistance to Bending | 650 | Mpa | ASTM D 790-90 |
| Bending Modulus | 27 | Gpa | ASTM D 790-90 |
| ILSS (Interlaminar Shear Strength) | 50 | Mpa | ASTM D 2344-84 |
| Specific Weight | 1 to 1.39 | ||
| Maximum Serviceable Temperature - Resin* | 446 - 230* | °F - °C | |
| Maximum Serviceable Temperature - Woven Fibers | 1112 - 600 | °F - °C |
*The Shim use is not affected by the possible disappearance of the resin, under the heat action.
References to standards |
The material complies as follows with the ABD 0031 official standard:
- classified A (ex ATS 1 000-001),
- FAR 25.853 for smoke density and toxicity.
According to the NF F 16-101 official standard, the product is classified:
- M1 for behavior in fire,
- F1 for smoke density and toxicity.
According to the NF P 85-501 official standard, the product is classified:
- M1 for behavior in fire.
The product also meets the characteristic requirements of the D6-51377 official standard as follows:
- for behavior in fire,
- for low smoke emission and low heat emission.
Available thicknesses for laminated shims in X.Fiber® |
| Specific Weight | Thicknesses of Laminations inches / mm | |||
|---|---|---|---|---|
| X.FIBER-Carbon® | X.FIBER-Glass® | .003 0,075 |
.004 0,1 |
.0043 0,11 |
| 1 | √ | |||
| 1,37 | √ | |||
| 1,39 | √ | |||
For more information:
<< Previous
X.FIBER® = Trademark Registered, Europe: Patent No. EP 1 444 094 B1, Canada: CA 2 464 337 C, US: Patent Pending.
X.FIBER-Carbon® = Trademark Registered.
X.FIBER-Glass® = Trademark Registered.